1.8909 en 10025-6 S500QL steel deal
Gangsteel supply high-strength structural steel plates en10025-6 S500QL,1.8909 steel plates in quenched and tempered heat treatment. S500QL usually called high-strength plates and en10025-6 S500QL are widely used in construction machinery and mining machinery. S500QL steel standard: EN 10025/6-2004 delivery status: quenched and tempered.
Grade 303Se indicates the grade of the steel, and in this case, it has a Se addition. ASTM A514 alloy metal plate is thought for its high yield energy, weldability, and toughness, even at low temperatures. It is a low carbon quenched and tempered alloy steel that may be a low-value, high performing materials for structural use and high wear machine applications. ASTM A514 plate metal has a min-yield power of one hundred ksi/690 MPa.ASTM A36 Hot Rolled Steel Plate – pisello Steel SupplierASTM A36 Hot Rolled Steel Plate.
1.8909 en 10025-6 S500QL cutting parts
en10025-6 S500QL 1.8909 steel suppliers near me
en10025-6 S500QL 1.8909 tube steel
en10025-6 S500QL 1.8909 metal steel
en10025-6 S500QL 1.8909 steel supplier
en10025-6 S500QL 1.8909 steel company
en10025-6 S500QL 1.8909 mild steel
en10025-6 S500QL 1.8909 steel sales
en10025-6 S500QL 1.8909 united states steel
en10025-6 S500QL 1.8909 tubular steel
en10025-6 S500QL 1.8909 free steel
en10025-6 S500QL 1.8909 steel supplies
en10025-6 S500QL 1.8909 steel manufacturers
en10025-6 S500QL 1.8909 honing steel
en10025-6 S500QL 1.8909 metalsdepot
en10025-6 S500QL 1.8909 steels
en10025-6 S500QL 1.8909 ussteel
en10025-6 S500QL 1.8909 steel shop
en10025-6 S500QL 1.8909 steel tube sizes
en10025-6 S500QL 1.8909 steel products
en10025-6 S500QL 1.8909 steel material
en10025-6 S500QL 1.8909 steelrs
en10025-6 S500QL 1.8909 steel tubes
en10025-6 S500QL 1.8909 steelers wheel
en10025-6 S500QL 1.8909 free steel
In these cases, the closest match comparison decisions had been made at the discretion of the editor. The designations apply to wrought products, e.g. sheet, bars, tubes, wires and for wrought components.
U.S. Steel to Buy Remaining Stake in New, Low-Cost Steel Mill – The Wall Street Journal
U.S. Steel to Buy Remaining Stake in New, Low-Cost Steel Mill.
Posted: Tue, 08 Dec 2020 15:22:00 GMT [source]
The chemical composition of structural metal is very important and extremely regulated. It is an important issue which defines the mechanical properties of the steel material. In the following desk, the chemical composition of S500 is displayed. bluing, n—subjecting the dimensions-free floor of a steel object to the motion of air, steam, or different agents at a suitable temperature, thereby forming a skinny blue movie of oxide and bettering the thing’s look and corrosion resistance. DISCUSSION—This time period is ordinarily utilized to sheet, strip, or finished components.
3. The chemical composition and mechanical properties of S500QL,1.8909 steel plates steel plates:
Carbon C: ≤0.20 Silicon Si: ≤0.80
Manganese Mn: ≤1.70 Nitrogen N: ≤0.015
Boron B: ≤0.0050 Chromium Cr: ≤1.50
Copper Cu: 0.50 Molybdenum Mo: 0.70
Niobium Nb: 0.06 Nickel Ni: ≤2.0
Titanium Ti: ≤0.05 Vanadium V: ≤0.12
Zirconium Zr: ≤0.15 S: ≤0.025
Phosphorus P: ≤0.015
PS: The specific chemical composition should be indicated in the steel plant material book.
en10025-6 S500QL 1.8909 metal suppliers online
2. en10025-6 S500QL,1.8909 are: S500Q, S500QL, S500QL1��Two, S500Q, S500QL, S500QL1 chemical composition: The quality of S500Q is divided into three level
Steel ETF surges to 52-week high. There is ‘room to the upside,’ but don’t chase, trader says – CNBC
Steel ETF surges to 52-week high. There is ‘room to the upside,’ but don’t chase, trader says.
Posted: Mon, 07 Dec 2020 12:05:00 GMT [source]
specified factor, n—in metal, an element controlled to a specified minimal, most, or range, in accordance with the requirements of the relevant product specification. stabilized stainless-steel, n—a chrome steel that conforms to a specification that prescribes limits for niobium , tantalum, titanium, or a combination thereof.
- isothermal annealing, n—austenitizing a metal object and then cooling it to, and holding it at, a temperature at which austenite transforms to a ferrite-carbide combination.
- nitriding, n—introducing nitrogen into a solid steel object by holding it at a suitable temperature involved with a nitrogenous surroundings.
- isothermal transformation, n—a change in section at any constant temperature.
- being quenched is faraway from the quenching medium whereas the thing is at a temperature substantially larger than that of the quenching medium.
Composition ranges for manganese and silicon and most percentages for sulfur and phosphorus are additionally specified. For alloy steels, the first two digits of the SAE system describe the main alloying parts current within the materials, the first digit giving the alloy group. For example the 43XX collection steels contain 1.sixty five–2.00 % Ni, 0.50–0.eighty % Cr and 0.20–0.30 % Mo, together with composition ranges for manganese and silicon and maximums for sulfur and phosphorus. Additional letters added between the second and third digits embody “B” when boron is added (between 0.0005 and 0.003 %) for enhanced hardenability, and “L” when lead is added (between 0.15 and 0.35 %) for enhanced machinability.
What is EN 10025-6 S500QL Equal Grade.
| Equivalent steel grade of S500QL CHINA Grade Q500E | |||
|
Europe |
Germany |
France |
Sweden |
|
FeE 500 V KT |
TStE 500 V |
E 500T |
2615 |
S500Q and S500QL steel plates are German standard high-strength structural steels, usually called high-strength plates, equivalent to the national standard Q500D,
It is widely used in construction machinery and mining machinery.
S500QL steel standard: EN 10025/6-2004 delivery status: quenched and tempered. S500Q series are: S500Q, S500QL, S500QL1.Second, S500Q chemical composition: The quality of S500Q is divided into three levels
What is EN 10025-6 S500Q mechanical properties?
EN10025-6 S500Q quenched and tempered steel plate mechanical properties
| Grade |
Thickness |
Min Yield (Mpa) |
Tensile (MPa) |
Elongation (%) |
Min Impact Energy |
|
|
EN10025-6 S500QL
|
8mm-50mm |
Min 500Mpa |
590-770Mpa |
17% |
-40 |
Min 30J |
|
51mm-100mm |
Min 480Mpa |
590-770Mpa |
17% |
-40 |
Min 30J |
|
|
101mm-150mm |
Min 440Mpa |
540-720Mpa |
17% |
-40 |
Min 30J |
What is application of EN10025-6 S500QL?
Used in buildings, bridges, ships, vehicles, pressure vessels and other structures, the carbon content (melting analysis) is generally not more than 0.20%, the total content of alloying elements is generally not more than 2.5%, the yield strength is not less than 295MPa, and it has good impact toughness
And low alloy steel with welding function.
What is EN 10025-6 S500QL chemical?
EN10025-6 S500QL quenched and tempered steel plate Chemical composition
| Grade |
C % |
Si % |
Mn % |
P % |
S % |
N % |
B % |
Cr % |
|
EN 10025-6 S500QL
|
0.200 |
0.800 |
1.700 |
0.020 |
0.010 |
0.015 |
0.005 |
1.500 |
|
Cu % |
Mo % |
Nb % |
Ni % |
Ti % |
V % |
Zr % |
|
|
|
0.500 |
0.700 |
0.060 |
2.000 |
0.050 |
0.120 |
0.150 |
|
Depending on the product thickness and manufacturing conditions, the manufacturer can add one or several alloying elements to the steel to increase the maximum value in order to obtain the specified properties (see 7.2.2).
At least 0.015% of grain refinement elements should be present. Aluminum is one of these elements.
The minimum content of soluble aluminum is 0.015%. If the aluminum content reaches the minimum of 0.018%, the value is considered to be reached.
isothermal annealing, n—austenitizing a steel object and then cooling it to, and holding it at, a temperature at which austenite transforms to a ferrite-carbide aggregate. isothermal transformation, n—a change in part at any fixed temperature. maraging, n—a precipitation hardening treatment applied to a particular group of alloy steels to precipitate one or more intermetallic compounds in a matrix of basically carbonfree martensite. pure aging, n—spontaneous aging of an excellent-saturated strong solution at room temperature.