Gangsteel produce and exported stainless steel plate ASTM A240 304LN UNS 30453, astm a240 304ln,astm a240 type 304ln,a240 304n material cutting parts,a240-304ln machine parts,a240 304ln flat bar ,a240 304ln welded pipe.

A240 304LN stainless steel plate oven Exporter

Applications by which processing tools is topic to each an aggressively corrosive environment and to cycle loading can profit from the properties of 2205 duplex stainless-steel plate. Because of its high chromium , molybdenum , and nitrogen (0.18) contents, the corrosion resistance properties of 2205 duplex stainless-steel plate are superior to that of 316L or 317L in most environments. The chromium, molybdenum, and nitrogen in 2205 duplex chrome steel plate also provide excellent resistance to pitting and crevice corrosion even in very oxidizing and acidic solutions. The high carbon content, which is current to enhance creep properties, has a detrimental impact on aqueous corrosion resistance. The alloy is vulnerable to intergranular corrosion after long run publicity at excessive temperatures.

In this temperature range, the general corrosion resistance of Alloy 347 chrome steel plate is superior to Alloy 321 stainless-steel plate. Alloy 347 also performs considerably higher than Alloy 321 in strongly oxidizing environments up to 1500°F (816°C). The alloy can be used in nitric solutions, most diluted natural acids at average temperatures and in pure phosphoric acid at decrease temperatures and up to 10% diluted solutions at elevated temperatures. Alloy 347 chrome steel plate resists polythionic acid stress corrosion cracking in hydrocarbon service. It can be utilized in chloride or luoride free caustic solutions at reasonable temperatures.

304LN stainless steel steel specifications: round bars, forged round bars, plates, sheets, forgings, plates, round bars, forged rounds, forgings, coils, strips, small round bars.304LN stainless steel steel price description: stainless steel, alloy steel sales price, mold steel price, steel price, sales price,304LN stainless steel The main nicknames of steel: stainless steel, alloy structural steel, structural steel, aluminum, steel, die steel, die material, wear-resistant plate.304LN stainless steel Metal material name: alloy steel, stainless steel, aluminum, spring steel, wear-resistant plate, high-speed steel, carbon steel., car light round, forged round, smooth round, cold rolled

A240 304LN stainless plate ring Exporter

Stilride, the Origami Steel e-Scooter With a Very Noble Purpose – autoevolution

Stilride, the Origami Steel e-Scooter With a Very Noble Purpose.

Posted: Mon, 16 Nov 2020 06:47:00 GMT [source]

LDX 2101 is a low-nickel; nitrogen enhanced lean duplex stainless steel developed for general-function use. The austenitic-ferritic construction of the alloy is balanced to approximately equal amounts of ferrite and austenite within the resolution-annealed condition. The excessive chromium and nitrogen content material of LDX 2101, combined with an addition of molybdenum, provide superb resistance to localized and uniform corrosion. The duplex microstructure contributes to the alloys excessive power and resistance to chloride stress-corrosion cracking.

Alloy 2304 is a 23% chromium, 4% nickel, molybdenum-free duplex stainless steel.
Different forms of chrome steel embrace the elements C from 0.03 to higher than 1.00, N, Al, Si, S, Ti, Ni, Cu, Se, Nb, and Mo).
Resistance to corrosion and marking, low upkeep, and acquainted luster make chrome steel a perfect materials for many applications where both the power of metal and corrosion resistance is required.
Alloy is a 23% chromium, 4% nickel, molybdenum-free duplex stainless-steel.
Specific forms of chrome steel are often designated by a 3 digit quantity.

The steel has glorious resistance to chloride stress corrosion cracking, high thermal conductivity and a low coefficient of thermal growth. Alloy 2507 is not really helpful for purposes which require long exposures to temperatures above 570°F because of the risk of a discount in toughness. About 21% of those are stainless steel sheets, 20% are stainless steel pipes, and 1% are bolts. Alloy 304/304H (UNS S30400/ S30409) is a modification of essentially the most broadly utilized “18-eight” chromium-nickel austenitic chrome steel. The carbon content material is controlled in the vary of 0.04-0.10% for increased power at temperatures above 800°F (427°C). SUS304 materials is a Japanese JIS standard and probably the most commonly used stainless steel, containing 18% Cr and 8% Ni. Alloy 347 stainless-steel plate is stabilized by the addition of columbium and tantalum.

A240 304ln stainless steel plate supplier at China

Gangsteel main grade is Main business: 440C, 2205, incoel718, suh660, 600 alloy, C276 alloy, Invar36, S31254, S30815, 11Cr17, S17400, F6NM, A286 alloy, Invar36, 0Cr17Ni4Cu4Nb, F6NM stainless steel, S21800, Nitronic60, S35750, S3276, high temperature alloys,

What is ASTM A240 304LN Stainless steel plate?
304LN stainless steel,Name: Austenitic stainless steel, Standards: AISI, ASTM, UNS Number: S30453 . 304LN features and applications: Austenitic stainless steel, equivalent to 00Cr19Ni10 or 0Cr18Ni10 in our country, is the most common stainless steel. It is often used to make home appliances and containers. It is also a heat-resistant steel. Our commonly used stainless steel kitchenware is made of 304. Stainless steel fasteners can also be made.

304 is a stainless-steel material of the American standard, astm is 304, uns is s30403, for Chinese 0ci19ni9, German standard w-nr 1.4301, Japan is sus304, the United Kingdom is 304s15

Compared with 304L steel, 304LN adds N to improve the high strength and grain boundary corrosion resistance of structural parts.
304LN stainless steel use: structural use, chemical substance transport ship.

Hastelloy, duplex stainless steel, corrosion resistant alloy, precipitation hardening steel, Monel, Inconel, heat resistant alloy, martensitic stainless steel, austenitic stainless steel, special steel, special steel

A240 304LN chemical list	Content (%)
Chromium, Cr	18-20
Nickel, Ni	8-12
Manganese, Mn	2 max
Silicon, Si	1 max
Nitrogen, N	0.1-0.16
Phosphorous, P	0.045 max
Carbon, C	0.03 max
Sulfur, S	0.03 max
Iron, Fe	Remainder

A240 304LN Properties	Metric	Imperial
Tensile strength	515 MPa	74694 psi
Yield strength	205 MPa	29732 psi
Elongation at break (in 50 mm)	40%	40%
Hardness, Brinell	217	217
Hardness, Rockwell B	95	95

A240 304LN STANDARDS
INDUSTEEL TRADEMARKS		UNS	ASTM	EURONORMS EN	SUS
UR™ 304LN		S30453	304LN	1.4311 X2CrNiN18-10	SUS 304LN
A240 304LN CHEMICAL ANALYSIS (%WEIGHT)
C	Cr	Ni	Mo	N	Others
< 0,030	18,5	8,5	–	0,15

A240 304LN PROPERTIES
0,2 Y.S. – Rp 0,2min ASTM / EN		0,2 Y.S. – Rp 0,2(2) typical value		UTS – Rm min ASTM / EN		UTS – Rm(2) typical value		EI-A(1)%	PREN(4)	HOMOLOGATIONS
MPa	Ksi	MPa	Ksi	MPa	Ksi	MPa	Ksi			Last revised
270	39	335	49	550	80	630	91	45	21

A240 304LN APPLICATIONS
CHEMICAL INDUSTRIES			PROCESS INDUSTRIES			WATER TREATMENT			STORAGE & TRANSPORTATION
Nitric Acid	Sulfuric Acid	Polymer & other acids	Fertilizers	Pulp & Paper	Hydrome-tallurgy	Sea water & desalination	Fresh water & Tanks	Waste Water	Chemical Tanks	Cryogenic Tanks	Renewable

Our production Equipment introduction 3500MM Steckel Mill

Walking-beam reheating furnace, high pressure descales, coiling furnace, edger, four-high reversing mill, ACC, coiling machine, hot leveler, disc-type cooling bed, on-line UT defect inspection device, cold leveler, shot blaster etc. Annual Production Capacity-steel plates:960,000 tons, steel coils:240,000 tons 。
3500production capacity and scope
1） Hot rolled steel plates ：
Thickness ：4.5 ～50 mm
Width：910 ～3,100 mm
Length：3,000 ～18,000 mm
Piece weight：max. 22.6 t
2） Hot rolled steel coil ：
Thickness：4.5 ～25 mm
Width：1,600 ～3,000 mm
Piece weight：max. 45 t
Inner/Outer diameter:762 ～2,150 mm

253MA does nonetheless have a excessive carbon content so is highly susceptible to sensitisation ferom welding or service publicity. 253MA S30815 Stainless Steel accommodates fairly lownickelcontent, which gives it some benefit in lowering sulphide atmospheres when in comparison with high nickel alloys and to Grade 310. The inclusion of high silicon, nitrogen and cerium contents provides thesteelgood oxide stability, excessive elevated temperature energy and wonderful resistance to sigma phaseprecipitation. Under valuable steerage of our skilled professionals, we are engaged in offering a variety ofBlack Steel Pipe.Owing to its outstanding high quality, the supplied metal pipe is highly applauded by our purchasers. Provided range is precisely designed by our professional professionals using excellent quality materials and advanced know-how. Moreover, we check the supplied steel pipe on various quality parameters to supply a flawless dispatch from our finish.

Gangsteel is the large factory who produce 304LN Stainless steel plate at China .304LN��S30453��UNS S30453��SUS304LN��1.4311��022Cr19Ni10N��00Cr18Ni10N. The adopt standard are GB/T24186-2009��GB/T20878-2007 ASTMA240/ASME SA-240 ASTMA276��ASTMA182/ASME SA-182��ASTMA312/ASMES A312��JISG4051��JISG4303��EN10028/2-2009

What is SUS304LN AND A240 304LN? SUS304LN corresponds to GB 00Cr18Ni10N and German DIN X2CrNiN1810. SUS304LN (18Cr-8Ni-N-low C) adds N to SUS304 steel to make it have the same performance as above. The purpose of SUS304LN stainless steel is the same as that of SUS304N1 steel, but its resistance to intergranular corrosion is better.
SUS304LN corresponds to GB 00Cr18Ni10N and German DIN X2CrNiN1810.

A240 304LN stainless plate houston Exporter

A240 304LN stainless steel plate oven Exporter

The important pitting temperatures of a number of high-efficiency steels in a 1M sodium chloride answer have been decided. The results illustrate the excellent resistance of 2507 to pitting corrosion. The normal knowledge unfold for every grade is indicated by the dark grey portion of the bar. The duplex structure of 2507 supplies wonderful resistance to chloride stress corrosion cracking .

A240 304LN stainless plate hook Exporter

Pitting needn’t be a risk in the zone under the borderline on this determine, however crevices have to be avoided. A Corrosion Resistant Austenitic Stainless Steel with a High Molybdenum and Nitrogen Content Developed for Use in Chloride Containing Environments. Alloy 317LMN is an austenitic chromium-nickel-molybdenum stainless steel with corrosion resistance superior to 316L and 317L. The greater molybdenum content, mixed with an addition of nitrogen, supplies the alloy with its enhanced corrosion resistance, especially in acidic chloride containing service. The mixture of molybdenum and nitrogen additionally improves the alloys resistance to pitting and crevice corrosion.

Contact Us

HENAN GANG IRON AND STEEL CO.LTD

Email: admin@gangsteel.com

Phone: whatsapp: 008613598879167

CN China

, ,

This grade can also be very ductile, and has good weld capability enabling its widespread usage in many purposes. Alloy 309/309S(UNS S30900/S30908) austenitic stainless steel is often used for elevated temperature functions. Its excessive chromium and nickel content material offers comparable corrosion resistance, superior resistance to oxidation, and the retention of a bigger fraction of room temperature strength than the frequent austenitic Alloy 304. Alloy 309 is an austenitic chrome steel developed to be used in high temperature corrosion resistance purposes.

The corrosion resistance of LDX 2101 is usually good making it suitable for use in a wide variety of functions. In most environments, it’s superior to 304L stainless-steel and similar to the molybdenum containing 316L stainless-steel. It should not be used at temperatures above 572F or for cryogenic service. Optimal mechanical properties may be obtained by subjecting the alloy to age hardening warmth A240 SS304LN supplier remedies. The corrosion resistance of Alloy 17-4PH is corresponding to 304 chrome steel in most environments & is usually superior to the 400 collection stainless steels. It is utilized in applications the place the combination of reasonable corrosion resistance and unusually high strength are required.

The alloy resists oxidation up to 1900°F (1038°C) beneath non-cyclic circumstances. Frequent thermal biking reduces oxidation resistance to roughly 1850°F (1010°C). Because of its high chromium and low nickel content, Alloy 309 could be utilized in sulfur containing atmospheres up to 1832°F (a thousand°C). The alloy is not recommended to be used in extremely carburizing atmospheres because it displays only reasonable resistance to carbon absorption. A solution annealing remedy at 2012 – 2102°F (1100 – 1150°C) will restore a level of toughness.309S is the low carbon model of the alloy.

A240 304LN 18-8 stainless plate Exporter

Gangsteel supply 304ln stock steel plate. SUS304LN (18Cr-8Ni-N-low C) adds N to SUS304 steel to make it have the same performance as above. The purpose of SUS304LN stainless steel is the same as that of SUS304N1 steel, but its resistance to intergranular corrosion is better. If you have requirement, please contact us by email.

A240 304LN stainless 410 plate Exporter

A240 304LN stainless plate ring Exporter

Stilride, the Origami Steel e-Scooter With a Very Noble Purpose – autoevolution

A240 304LN stainless plate houston Exporter

A240 304LN stainless plate hook Exporter

A240 304LN 18-8 stainless plate Exporter

You May Also Like

astm a240 tp 316

a240 usn s30453

astm a240 grade 316l